Measurements of the surface tension (gamma LV) and advancing contact angle (theta) on poly( tetrafluoroethylene) (PTFE) were carried out for aqueous solutions of cetyltrimethylammonium bromide (CTAB), cetylpyri-dynium bromide (CPyB), sodium decylsulfate (SDS), sodium dodecylsulfate (SDDS), p-(1,1,3,3-tetramethylbutyl) phenoxypoly(ethylene glycol)s, Triton X-100 (TX100) and Triton X-165 (TX165) and their mixtures. The results obtained indicate that the values of the surface tension and wettability of PTFE depend on the concentration and composition of the surfactants mixture. In contrast to Zisman finding, there was no linear dependence between cos. and the surface tension of aqueous solutions of surfactants and their mixtures for all studied systems, but a linear dependence existed between the adhesional tension and solution surface tension for PTFE in the whole concentration range, the slope of which was -1, indicating that the surface excess concentration of surfactant at the PTFE-solution interface was the same as that at the solution-air interface for a given bulk concentration. It was also found that the work of adhesion of aqueous solutions of surfactants and their mixtures to PTFE surface did not depend on the type of surfactant, its concentration and composition of the mixture. This means that for the studied systems the interaction across PTFE-solution interface was constant, and it was largely of Lifshitz-van der Waals type. On the basis of the surface tension of PTFE and the Young equation and thermodynamic analysis of the work of adhesion of aqueous solutions of surfactants to the polymer surface it was found that in the case of PTFE the changes of the contact angle as a function of the total mixture concentration in the bulk phase resulted only from changes of the polar component of the solution surface tension. (C) Koninklijke Brill NV, Leiden, 2008