The use of a Pt catalysed H-2-diffusion anode for Ni electrowinning has been studied from typical chloride, Watts and sulfate baths at 25 degrees C. Higher anodic current densities are found in a three-electrode cell when sulfate ions are gradually replaced by chloride ions. Adherent Ni deposits are obtained from the Watts and sulfate media, whereas in the chloride bath, Cl-2 is released at the anode and less adherent deposits are formed. Current efficiencies between 94 and 98 for anodic current densities ranging from 15 to 65 mA cm(-2) have been found. The energy costs for Ni electrowinning decrease with increasing chloride content in the bath, and their values are always much lower than those reported using conventional DSA, graphite or lead anodes. All deposits are composed of high-purity Ni, free of heavy metals and other impurities. The crystals have a face-centred cubic structure with a preferential orientation which mainly depends on the medium and current density. A superimposed magnetic field of 0.9 T orientated either parallel or perpendicular to electrodes in a two-electrode cell exerts only a small effect on the crystallographic orientation of Ni, although it has a certain influence on its morphology.