Polycrystalline samples of La0.8Ca0.2Fe0.8Ni0.2O3-delta (LCFN) with perovskite type structure have been prepared by combustion, freeze drying, citrate-gel process and liquid mix method. The analysis of X-ray powder diffraction indicated that the samples were single phase and crystallized in an orthorhombic (space group, Pnma no. 62) structure. Transmission electron microscopy (TEM) analysis on the synthesized powder at 600 degrees C by liquid mix method showed clusters of 150 nm formed by nanoparticles of 20 nm. Electrochemical performance of LCFN cathodes, which are used for intermediate temperature solid oxide fuel cells, were investigated. The polarization resistance was studied using two different electrolytes: Y-doped zirconia (YSZ) and Sm-doped ceria (SDC). The dc four-probe measurement exhibits a total electrical conductivity, over 100 S cm(-1) at T >= 600 degrees C, pointing out that strontium can be substituted for the cheaper calcium cation without destroying the electrochemical properties. Experimental results indicate that nanoparticles have more advantages in terms of smaller particle size and better electrochemical performance. (C) 2010 Elsevier Ltd. All rights reserved.