The blends of polyethersulfone and phenoxy were prepared by melt mixing in a Brabender-like apparatus. The specimens for measurements were made by compression molding and then were water-quenched at room temperature under pressure. The tensile strength, tensile modulus, elongation at break and yield, density, thermal analysis, and dynamic mechanical properties were each measured. The dependence of tensile strength, tensile modulus, elongation at break and yield, and density on composition was obtained. The relationship between tensile modulus and elongation at break and yield and speed of the crosshead at different weight ratios of the blends is shown. The effects of composition and miscibility on the mechanical properties are discussed.