Novel high glass transition temperature polyaryletherketones, containing pendant amido, alkyl, and carboxyl groups with reduced viscosity above 0.54 dL/g, were synthesized via solution nucleophilic polycondensation reaction of phenolphthalin, 2’,2 "-diisopropyl-5’,5 "-dimethylphenolphthalin, and 3,3’-bis(4-hydroxyphenyl)isobenzopyrrolidone with bis(4-nitrophenyl)ketone in the presence of potassium carbonate. By ion exchange with Na+ and K+, four ionomers were also prepared. A new monomer simultaneously containing carboxyl and algyl substituents was synthesized by reduction reaction of 2’,2 "-diisopropyl-5’,5 "-dimethyl-phenolphthalein. The resulting polymers were soluble in a few polar aprotic solvents; transparent, colorless, and tough films could easily be cast from DMF or DMSO solution. The mechanical properties of the films were excellent; and their tensile strength, elongation at break, and tensile moduli were in the range of 67.1-97.1 MPa, 7.8-165%, and 1.47-2.27 GPa, respectively. The prepared polymers showed fairly good thermal stability and resonably high glass transition temperatures above 210 degrees C.