A hybrid junction solar cell with amorphous silicon (a-Si) and multicrystalline silicon (mc-Si) was fabricated using a mc-Si sheet substrate, which is produced directly from molten silicon using a novel rotational solidification method. The efficiency of 11.6% was obtained for the hybrid junction cell, while 10.2% for the single junction cell made of a mc-Si sheet substrate, which confirmed that the hybrid structure is effective to improve the solar cell property made of a mc-Si substrate. With introducing light trapping structure, the efficiency was improved to be 12.0%. Moreover, the possibility of Jsc improvement was investigated using the advanced light trapping structure. Jsc of 15.6 mA/cm(2) was obtained and it was confirmed that the hybrid junction is a promising structure. (C) 2002 Elsevier Science B.V. All rights reserved.