Nanocrystalline titanium carbide (TiC) thin films were prepared by magnetron sputtering deposition at 473 K. The effect of substrate bias on microstructure and mechanical properties was studied in details using X-ray photoelectron spectroscopy, X-ray diffraction, field emission scanning electron microscopy, indentation and scanning microscratch. The TiC films exhibit a (111) preferential orientation. Substrate bias decreases grain size and deposition rate of the TiC films. The TiC films have columnar structure which becomes finer at high substrate bias. Nanoindentation hardness, Young's modulus, and toughness of the films are increased as the substrate bias goes up. However, the adhesion peaks at substrate bias of -100 V and drops when bias is increased further. (c) 2007 Elsevier B.V. All rights reserved.