Cuprous oxide (Cu(2)O) and cupric oxide (CuO) thin films were deposited on glass substrates at different oxygen partial pressures by direct-current reactive magnetron sputtering of pure copper target in a mixture of argon and oxygen gases. Oxygen partial pressure was found to be a crucial parameter in controlling the phases and, thus, the physical properties of the deposited copper oxide thin films. Single-phase Cu(2)O thin films with cubic structure were obtained at low oxygen partial pressure between 0.147 Pa and 0.200 Pa while higher oxygen partial pressure promoted the formation of CuO thin films with base-centered monoclinic structure. Polycrystalline Cu(2)O thin films deposited with oxygen partial pressure at 0.147 Pa possessed the lowest p-type resistivity of 1.76 Omega cm as well as an optical band gap of 2.01 eV. On the other hand, polycrystalline CuO thin films deposited with oxygen partial pressure at 0.320 Pa were also single phase but showed a n-type resistivity of 0.19 Omega cm along with an optical band gap of 1.58 eV. (C) 2009 Elsevier B.V. All rights reserved.