Pyrene and 1-pyrenebuturic acid molecules were deposited on glass and copper substrates with the formation of submicron dots by laser-induced molecular micro-jet implantation through polar and non-polar liquid layers. The size of the smallest 1-pyrenebuturic acid molecules dots prepared on a glass substrate by implantation through water and diiodomethane was estimated to be about 400 nm and 300 nm at laser fluences of 235 J/cm(2) and 326 J/cm(2), respectively. The fluorescence and the Raman spectra showed that the implanted 1-pyrenebutyric acid molecules did not decompose during the implantation process. The smallest size of a pyrene dot was 700 nm at the laser fluence of 378 J/cm(2). However, the pyrene dots could be formed only by implantation through a water layer. (C) 2009 Elsevier B.V. All rights reserved.