Hydrogen-free diamond-like carbon (DLC) films were prepared by means of microwave electron cyclotron resonance plasma enhanced direct current magnetron sputtering. To study the influence of enhanced plasma on film fabrication and properties, the structures as well as mechanical and electrical properties of these films were studied as a function of applied microwave power. Results showed that higher microwave power could induce higher plasma density and electron temperature. The hardness increased from 3.5 GPa to 13 GPa with a variation of microwave power from 0 W to 1000 W. The resistivity showed a drastic increase from 4.5 x 10(4) Omega cm at 0 W to 1.3 x 10(10) Omega cm at 1000 W. The variation of the intensity ratio I(D)/I(G) and the position of the G-peak of the DLC films with respect to changes in microwave power were also investigated by Raman spectroscopy. (C) 2010 Elsevier B.V. All rights reserved.