The results of the electric and magnetic measurements performed on PbZr0.2Ti0.8O3-BiFeO3 symmetric structures, deposited on Pt/Si wafers, were compared for different number of layers in order to analyse the effect of interfaces over the macroscopic properties. It was found that the shape and magnitude of the capacitance-voltage characteristic, as well as the shape and parameters of the ferroelectric and magnetic hysteresis, depend on the number of interfaces in the intended multilayer structure. A temperature induced gradual transition from a magnetically disordered spin glass like phase of low temperature to an uncompensated antiferromagnetic phase at room temperature takes place in the BiFeO3 films, under low applied magnetic fields. A partial ferromagnetic like order can be obtained at low temperatures by increasing the field. The observed changes in the electric and magnetic behaviour of the systems were related to an increased degree of disorder for electric dipoles and magnetic moments, due to the increased number of layers and crystallization treatments. (C) 2011 Elsevier B.V. All rights reserved.