The influence of the solvent and annealing temperature on the field-effect mobilities and morphologies of poly(3-hexylthiophene)-b-poly(gamma-benzyl-L-glutamate) (P3HT-b-PBLG) rod-rod diblock copolymer has been investigated. Thin film X-ray diffraction studies show peaks originating from both P3HT and PBLG indicating that the crystalline nature of both the blocks is conserved after the formation of the block copolymer. It has been observed that the field-effect mobilities of the diblock copolymer are independent of the annealing temperatures for thin films deposited from both 1,2,4-trichlorobenzene and chloroform solvents. The correlation between the field-effect mobility and morphology indicates that the P3HT block self-assembles at the surface SiO2 dielectric.