Nanocrystalline high surface area Mn3O4 powder was obtained at low temperature by a solvent-free route. The precursor was a mixture of manganese (II) acetate, 3,6,9-trioxadecanoic acid (TODA) and ammonium acetate that were intimately mixed by grounding in an agate mortar. Nanocrystalline Mn3O4 was obtained by thermal treatment at 120 degrees C. Powder X-ray diffraction, selected area electron diffraction, high resolution transmission electron microscopy, and Fourier transformed infrared characterization confirmed the formation of the hausmannite phase. The as-prepared mesoporous material has high specific surface area (120 m(2) g(-1)). The performances of tape casted Mn3O4 nanopowder electrodes were investigated as anode material for lithium ion batteries. High capacity values were achieved at diverse C rates. Capacity fading was found to be dependent on the upper cut off voltage, the presence of a plateau at 2.25 V vs. Li+/Li being detrimental for long term cyclability. (C) 2012 Elsevier Ltd. All rights reserved.