Thick electrophoretically deposited (EPD) films of ligand-capped colloidal nanocrystals (NCs) typically crack when removed from the deposition solvent due to the loss of residual solvent. We report the suppression of fracture in several micrometers thick EPD films of CdSe NCs by treating the wet, as-deposited films with solutions of polymer precursor monomers, followed by UV-initiated polymerization. The monomers diffuse into voids and, for several monomers, dissolve the NCs to form a uniform dispersion in the film.