Nanometer Cu-substituted alpha-nickel hydroxide was synthesized by means of ultrasonic-assisted precipitation. Particle size distribution (PSD) measurement, X-ray diffraction (XRD), and high-resolution transmission electron microscope (HR-TEM) were used to characterize the physical properties of the synthesized samples. The results indicate that the average particle size of the samples is about 96-110 nm and the XRD diffraction peaks are anisotropic broadening. The crystal grains are mainly polycrystal structure with columnar or needle-like morphology, containing many defects. With increase of Cu content, the shape of primary particles transform from columnar to needle-like. The influences of doping amounts of Cu on the electrochemical performance were investigated through constant current charge/discharge and cyclic voltammetric measurements. The specific capacity increases initially and then decreases with increasing Cu-doping ratio, the electrode C containing 0.9 wt.% Cu shows the maximum discharge capacity of 310 mAh/g at 0.2 C, and it has the lowest charging voltage, higher discharge voltage plateau, better cycle performance and larger proton diffusion coefficient than the other electrodes. (c) 2012 Elsevier Ltd. All rights reserved.