Most industrially relevant high temperature gas separations (>= 150 degrees C) of either carbon dioxide (flue gas) or hydrogen (syn-gas) must be performed in the presence of water vapor. At ambient temperatures, water vapor can permeate easily through most polymeric membranes and can influence the permeation of other gases through interaction with the polymer, such as swelling and clustering. At higher temperatures, water vapor can be destructive to polymer membranes by changing the polymer structure that can result in diminished gas separation performance. Little data has been reported on the influence of water vapor in gas separations at >100 degrees C because most polymers are not stable at temperature. Many high performance (HP) polymers are able to endure high temperatures and aggressive chemical conditions. For example, polyimides are promising HP polymers that effectively separate permanent gases at temperatures higher than 150 degrees C under dry conditions. In this report, the analysis of selected HP polymers in humidified gas streams (2-4 vol% water) shows that they can perform modest separations at ambient temperatures. In general, it was observed that water vapor permeability is greater than other tested gases. Additionally, the permeabilities of the analyte gases were somewhat influenced by the presence of humidity and their selectivities were significantly lower, as compared to corresponding experiments performed in the absence of water. To elucidate the role of water vapor in gas transport, energy of activation of permeation (E-p) values were obtained for Matrimid 5218 from 30-200 degrees C in a humidified mixed gas stream, and it was found that the selectivities are nearly identical to dry gas streams at 150 degrees C. This data suggests that water vapor functions as a gas and only slightly decreases selectivity of the other gases at elevated temperatures. As a result, economic wet gas separations may be possible using these materials if the gas stream is kept at higher temperature (>150 degrees C), which is assisted by the inherent stability of the membranes.