TiNb2O7 and TiTa2O7 phases are synthesized by solid-state reaction method and are investigated for electrochemical Li insertion/extraction. The electrochemical insertion of Li in these phases is characterized by both solid solution and two-phase regimes. The structure is stable toward Li insertion/extraction. The first cycle discharge capacity values are 307 mAh g(-1) and 215 mAh g(-1) in the voltage range of 3.0-1.0 V for TiNb2O7 and TiTa2O7 phases, respectively. The discharge capacities of TiNb2O7 and TiTa2O7 are 212 mAh g(-1) and 100 mAh g(-1), respectively, after 20 cycles. (C) 2013 Published by Elsevier Ltd.