Journal of Industrial and Engineering Chemistry, Vol.19, No.6, 2004-2009, November, 2013
DOI10.1016/j.jiec.2013.03.013  Export Citation
Corrosion inhibition and Biocidal effect of some cationic surfactants based on Schiff base
Samy M. Shaban†, Atef Saied, Salah M. Tawfik, A. Abd-Elaal, and Ismail Aiad
  • Egyptian Petroleum Research Institute, EPRI, Cairo, Egypt
E-mail:
The three cationic surfactants based on Schiff base were laboratory prepared, (E)-decyl-4-[(2- hydroxyethylamino) methyl]-N,N-dimethyl benzenaminium bromide (I), (E)-dodecyl-4-[(2-hydroxyethylamino)methyl]-N,N-dimethyl benzenaminium bromide (II) and (E)-hexadecyl-4-[(2-hydro-xyethylamino)methyl]-N,N-dimethyl benzenaminium bromide (III) were evaluated as corrosion inhibitors for carbon steel in acid medium and antimicrobial agents against sulfate reducing bacteria, SRB. Three techniques were used for the corrosion inhibition evaluation, namely; weight loss, polarization and electrochemical impedance. The serial dilution method was used to evaluate the inhibiting effect of these compounds on the sulfate reducing bacteria growth. The results showed that the prepared compounds have good antimicrobial activities against the SRB as well as they have high efficiency as corrosion inhibitors for carbon steel in 1 M HCl.
Keywords:Cationic surfactants;Corrosion inhibition;Sulfate reducing bacteria
  1. Scattergood GL, Corrosion Inhibitors for Crude Oil Refineries, Corrosion, ASM Handbook, 13, Macmillan, New York (1992)
  2. Amin MA, El-Rehim SSA, El-Sherbini EEF, Bayoumi RS, Electrochim. Acta, 52(11), 3588 (2007)
  3. Okafor PC, Zheng YG, Corrosion Science., 51, 850 (2009)
  4. Okafor PC, Liu X, Zheng YG, Corrosion Science., 51, 761 (2009)
  5. Quraishi MA, Sharma HK, Materials Chemistry and Physics., 78, 18 (2002)
  6. Quraishi MA, Jamal D, J. Appl. Electrochem., 32(4), 425 (2002)
  7. Quraishi MA, Khan MAW, Ajmal M, Anti-Corrosion Methods and Materials., 43, 5 (1996)
  8. Abdel Nabey BA, Khamis E, Ramadan MS, El Gindy A, Corrosion., 52, 671 (1996)
  9. Muralidharan S, Iyer SVK, Anti-Corrosion Methods and Materials., 44, 100 (1997)
  10. Cerchiaro G, Aquilano K, Filomeni G, Rotilio G, Cirioio MR, Ferreira AMDC, Journal of Inorganic Biochemistry., 99, 1433 (2005)
  11. Vancoa J, Svajlenova O, Racanskac E, Muselika J, Valentova J, Journal of Trace Elements in Medicine and Biology., 18, 155 (2004)
  12. Negm NA, Amouna S, Journal of Surfactants and Detergents., 11, 215 (2008)
  13. McDonnell G, Russell AD, Clinical Microbiology Reviews., 12, 147 (1999)
  14. Aiad I, Negm N, Journal of Surfactants and Detergents., 12, 313 (2009)
  15. Popova A, Sokolova E, Raicheva S, Christov M, Corrosion Science., 45, 33 (2003)
  16. Solmaz R, Kardas G, Culha M, Yazici B, Erbil M, Electrochim. Acta, 53(20), 5941 (2008)
  17. Behpour M, Ghoreishi SM, Soltani N, Niasari MS, et al., Corrosion Science., 50, 2172 (2008)
  18. Bentiss F, Lebrini M, Vezin H, Lagrenee M, Mater. Chem. Phys., 87(1), 18 (2004)
  19. Shen CB, Wang SG, Yang HY, Long K, Wang FH, Appl. Surf. Sci., 253(4), 2118 (2006)
  20. Zhang Z, Chen S, Li Y, Li S, Wang L, Corrosion Science., 51, 291 (2009)
  21. ASTM G1-72 (reapproved 2004), practice for preparing, cleaning and evaluating corrosion test specimens (1990)
  22. Lehr IL, Saidman SB, Electrochim. Acta, 51(16), 3249 (2006)
  23. Negm NA, Aiad I, Journal of Surfactants and Detergents., 10, 87 (2007)
  24. ASTM G3-89, standard practice for conventions applicable to electrochemical measurements in corrosion testing (1994)
  25. ASTM D4412-84 standard test methods for sulfate-reducing bacteria in water and water-formed deposits (2009)
  26. Osman MM, El-Ghazawy RA, Al-Sabagh AM, Mater. Chem. Phys., 80(1), 55 (2003)
  27. Keera ST, Deyab MA, Colloids and Surfaces A: Physicochemical and Engineering Aspects., 266, 129 (2005)
  28. Nataraja SE, Venkatesha TV, Manjunatha K, Boja Poojary MK, Pavithra HC, Tandon, Corrosion Science., 53, 2651 (2011)
  29. Nataraja SE, Venkatesha TV, Manjunatha K, Poojary B, Pavithra MK, Tandon HC, Corrosion Science., 53, 2651 (2011)
  30. Ahamad I, Gupta C, Prasad R, Quraishi MA, J. Appl. Electrochem., 40(12), 2171 (2010)
  31. Wu TX, Li ZJ, Zhao JC, Chemical Journal of Chinese Universities., 19, 1617 (1998)
  32. Wang J, Cao C, Chen J, Zhang M, Ye G, Lin H, Journal of Chinese Society for Corrosion and Protection., 15, 241 (1995)
  33. Lorenz WJ, Mansfeld F, Corrosion Science., 21, 647 (1981)
  34. Elkadi L, Mernari B, Traisnel M, Bentiss F, Lagrene´ e M, Corrosion Science., 42, 194 (2000)
  35. Prabhu RA, Venkatesha TV, Shanbhag AV, Kulkarni GM, Kalkhambkar RG, Corrosion Science., 50, 3356 (2008)
  36. Haruyama S, Tsuru T, Gijutsu B, Journal of the Japanese Society of Corrosion Engineering., 27, 573 (1978)
  37. Ramesh Saliyan V, Corrosion Science., 50, 55 (2008)
  38. Atta AM, El-Azabawy OE, Ismail HS, Hegazy MA, Corrosion Science., 53, 1680 (2011)
  39. Aiad IA, Badawi AM, El-Sukkary MM, El-Sawy AA, Adawy AI, Journal of Surfactants and Detergents., 15, 223 (2012)
  40. Koch A, Clinical Microbiology Reviews., 16(4), 673 (2003)
  41. Hugenholtz P, Genome Biology., (PMID 11864374), reviews 0003.1- 0003.8, http://genomebiology.com/content/pdf/gb-2002-3-2-reviews0003.pdf., 3(2) (2002)
  42. Walsh F, Amyes S, Current Opinion in Microbiology., 7(5), 439 (2004)
  43. Jamora C, Theodoraki MA, Malhotra V, Theodorakis EA, Bioorganic & Medicinal Chemistry., 9(6), 1365 (2001)