The present work provides scientific support on the use of latex of Ficus carica to synthesize stable silver nanoparticles (AgNPs). AgNPs synthesized immediately after the addition of latex to silver nitrate solution at room temperature. Synthesized nanoparticles were of spherical shape with average size of 163.7 nm. Fourier transform infrared spectroscopy analysis revealed capping of proteins and phenolic compound on AgNPs, while X-ray diffraction analysis confirmed the fcc nature of AgNPs. Particles formed were stable for a long time (6 months). It was found that incorporation of AgNPs with 2 and 4 % concentration exhibits synergistic increase in sun protection factor of commercial sunscreen and natural extracts ranging from 01 to 12,175 % than control. Further characterization of latex and AgNPs revealed total phenolic content of 98.75 and 94.88 mu g/ml. The ferric ion reduction potentials of latex and AgNPs were 79.69 and 18.79 %. Reduction potential of ascorbic acid was synergistically increased after cumulative preparation of ascorbic acid with latex and AgNPs and found to be 106.76 and 101.50 % for ascorbic acid + latex and ascorbic acid + AgNPs, respectively.