The development of new polymeric materials aimed to control the bacterial biofilm appears to be an important practical approach. The goal of the present study was to prepare and characterize poly(ethylene-co-vinyl acetate) copolymer (EVA) films containing citronellol, eugenol, and linalool and evaluate their efficiency on growth and biofilm formation of Listeria monocytogenes, Staphylococcus aureus, Staphylococcus epidermidis, Escherichia coli, and Pseudomonas aeruginosa in monospecies and dual species. The results showed that the addition of oil components influenced the elastic modulus (15 % decrease), the tensile stress (30 % decrease), the elongation at break (10 % increase), and the contact angle values (10-20A degrees decrease) while leaving the homogeneity of the surface unaltered. Among the polymeric films, EVA + citronellol and EVA + eugenol at 7 wt% had the best inhibitory effect. After 24-48 h of incubation, EVA + citronellol was more effective against the growth (30-60 % reduction) than EVA + eugenol (15-30 % inhibition). However, this inhibition decreased after 240 h of incubation. On the contrary, the biofilm evaluation revealed a strong inhibition trend also after prolonged incubation time: the amount of biomass per square centimeter formed on copolymer with oil components was significantly less (40-70 % decrease) than that on pure copolymer control for L. monocytogenes, S. aureus, and E. coli. When polymeric materials were simultaneously inoculated with combinations of S. aureus and E. coli, the biomass accumulated was higher for EVA + citronellol and lower for EVA + eugenol than that in monoculture biofilm. The findings were similar to the results obtained by 2,3-bis[2-methyloxy-4-nitro-5-sulfophenyl]-2H-tetrazolium-5-carboxanilide assay that measures the metabolic activity of viable cells.