Journal of Adhesion Science and Technology, Vol.27, No.22, 2421-2432, 2013
Curing kinetics of nano cupric oxide (CuO)-modified PF resin as wood adhesive: effect of surfactant
The effect of nano cupric oxide (CuO) in combination with surfactants on the curing kinetics of phenol-formaldehyde (PF) resin, as well as the bonding strength of plywood prepared using the modified resin was investigated in this study using dynamic and isothermal differential scanning calorimetry. The result showed that the incorporation of nano CuO along with alkane surfactant made in the laboratory clearly reduced the apparent activation energy of the PF resin and improved the addition and condensation reactions of the PF resin. Inclusion of the surfactant had the further effect of compensating the influence of diffusion control caused by nano CuO alone. The shear strength of plywood suggested that the addition of nano CuO (1%) alone or in combination with alkane surfactant (0.55%) or sodium lignosulfonate (0.55%) in the PF resin mixture was sufficient to meet the requirement of wood-based composites manufacturing.
Keywords:phenol-formaldehyde resin;nanosize cupric oxide;surfactant;curing kinetics;differential scanning calorimetry (DSC)