High strength, stimuli-responsive poly(acrylamide) composite hydrogels (PAAm CH gels) were prepared by grafting polymerization of acrylamide (AAm) onto temperature-sensitive core-shell microgels. These microgels, composing of poly(N-isopropylacrylamide) as core and polyvinylamine (PVAm) as shell, were used as both initiator and crosslinker to form a robust three-dimensional network via bonding the poly(acrylamide) (PAAm) backbone. The CH gels exhibited a remarkably rapid shrinking rate and transmittance switch in response to the environmental temperature change, which the conventional chemically cross-linking PAAm hydrogels (PAAm OR) were short of. Even compared to the bulk PNIPAAm hydrogels (PNIPAAm OR) crosslinked with N,N'-methylenebisaciylamide (MBA), the CH gels were featured with faster responsive rate, which could be attributed to the formation of interconnected water transportation channels between the microspheres and PAAm gel matrix due to the fast shrinking of microgels. Moreover, the effects of microgel species and content on swelling and mechanical properties of CH gels were also systematically investigated. The results elaborated that the CH gels could be compressed almost 99% without breaking and completely recovered their original shape when the stress was removed. And the optimized compressive strength of CH gels could be up to 21.94 MPa. Based on the analysis of CH gel mechanical properties, the influence of microsphere content on effective network chains density of CH gels was discussed through rheology measurements. Finally, the essential reinforcement on mechanical properties was mainly contributed to the homogeneous microstructure of hydrogel network and the energy dissipation mechanism of microgels in gel matrix. (C) 2013 Elsevier Ltd. All rights reserved.