Well-controlled sub-unit-cell layer-bylayer epitaxial growth of spinel alumina is achieved at room temperature on a TiO2-terminated SrTiO(3)single-crystalline substrate. By tailoring the interface redox reaction, 2D electron gases with mobilities exceeding 3000 cm 2 V-1 s(-1) are achieved at this novel oxide interface.