A novel nitrogen-doped P25-TiO2 of bimodal structure with activated carbon supported (N-P25-TiO2/AC) was synthesized via the modified sol-gel techniques. Besides adding urea as N-source, the N-doping could also be induced through calcination under mixed NH3/N-2 atmosphere. The composite was characterized using XRD, porosimetry, UV-vis spectrophotometry, FTIR, XPS, SEM/EDX and TEM. The physical stability of the composite was examined through ultrasonication disruption, and the composite exhibited good physical stability. The synergistic effects of the adsorption-solar photocatalysis of sulfamethazine (SMZ) as exhibited by the composites were examined. The best performing bimodal composite was N-P25-TiO2 (25 + 10)/AC, which comprised 25% of N-P25 and 10% N-TiO2 (so!) by weight composition (wt%). The maximum adsorption capacity (S-max) for the N-P25-TiO2 (25 + 10)/AC, at pH 3.0, 6.0 and 10.0 was 183 +/- 3, 194 +/- 3, and 103 +/- 2 mg g(-1), respectively. The effects of the total loading of N-doped titania, sol-gel synthesis technique, weight distribution of N-P25 and N-TiO2 (sol), composite dosage, light wavelength spectrum and solution pH on the photocatalytic degradation (PCD) of SMZ were investigated. The N-P25-TiO2 (25 + 10)/AC composite exhibited enhanced PCD efficiency under solar irradiation with a pseudo first-order rate constant (k(app)) of 0.48 h(-1), as compared to other types of bimodal composites because its higher N-P25 content led to a greater photocatalytic activity. (C) 2012 Elsevier B.V. All rights reserved.