Interfacial durability and electrical properties of CNT (carbon nanotube) or ITO (indium tin oxide) coated PVDF (poly(vinylidene fluoride)) nanocomposites were investigated for self-sensor and micro-actuator applications. The electrical resistivity of nanocomposites and the durability of interfacial adhesion were measured using a four points method during cyclic fatigue loading. Although the CNT/PVDF nanocomposites exhibited lower electrical resistivity due to the inherently low resistivity of CNT, both composite types showed good self-sensing performance. The durability of the adhesion at the interface was also good for both CNT and ITO/PVDF nanocomposites. Static contact angle, surface energy, work of adhesion, and spreading coefficient between either CNT or ITO and PVDF were determined as checks to verify the durability of the interfacial adhesion. The actuation performance of CNT or ITO coated PVDF specimens was determined through measurements of the induced displacement using a laser displacement sensor, while both the frequency and voltage were changed. The displacement of these actuated nanocomposites increased with increasing voltage and decreased with increasing frequency. CNT/PVDF nanocomposites exhibited better performance as self-sensors and micro-actuators than did ITO/PVDF nanocomposites. (C) 2013 Elsevier B. V. All rights reserved.