A novel hybrid system has been investigated based on polyaniline/carbon nanofiber (Pani/CNF) electrospun nanofibers for modification of gas diffusion electrode (GDE) in proton exchange membrane fuel cells (PEMFC). Pani/CNF hybrid nanofibers were synthesized directly on carbon paper by electrospinning method. For preparation of catalyst ink, 20 wt.% Pt/C electrocatalyst with a platinum loading of 0.4 mg cm(-2) was prepared by polyol technique. SEM studies applied for morphological study of the modified GDE with hybrid nanofibers. This technique indicated that the electrospun nanofibers had a diameter of roughly 100 nm. XRD patterns also showed that the average size of Pt nanoparticles was about 2 nm. Subsequently, comparison of the hybrid electrode electrochemical behavior and 20 wt.% Pt/C commercial one was studied by cyclic voltammetry experiment. The electrochemical data indicated that the hybrid electrode exhibited higher current density (about 15 mA cm(-2)) and ESA (160 m(2) gr(-1)) than commercial Pt/C with amount of about 10 mA cm(-2) and 114 m(2) gr(-1), respectively. The results herein demonstrate that Pani/CNF nanofibers can be used as a good alternative electrode material for PEMFCs. (C) 2014 Elsevier B. V. All rights reserved.