f polymerization of resorcinol-formaldehyde (RF) mixtures in water with addition of different amounts of zinc acetate and then carbonization of dried gels are studied to prepare ZnO doped chars. Zinc acetate as a catalyst of resorcinol-formaldehyde polycondensation affects structural features of the RF resin (RFR) and, therefore, the texture of chars prepared from Zn-doped RFR. The ZnO doped chars are characterized using thermogravimetry, low temperature nitrogen adsorption/desorption, Raman spectroscopy, X-ray diffraction (XRD), scanning electron microscopy (SEM), and high resolution transmission electron microscopy (HRTEM). At a relatively high content of zinc acetate ( Polycondensation polymerization of resorchial-formaldehyde (RF) mixtures in water with addition of different amounts of zinc acetate and then carbonization of dried gels are studied to prepare ZnO doped chars. Zinc acetate as a catalyst of resorcinol-formaldehyde polycondensation affects structural features of the RF resin (RFR) and, therefore, the texture of chars prepared from Zn-doped RFR. The ZnO doped chars are characterized using thermogravimetry, low temperature nitrogen adsorption/desorption, Raman spectroscopy, X-ray diffraction (XRD), scanning electron microscopy (SEM), and high resolution transmission electron microscopy (HRTEM). At a relatively high content of zinc acetate (1 mol per 10-40 mol of resorcinol) in the reaction mixture, the formation of crystallites of ZnO (zincite) occurs in a shape of straight nanorods of 20-130 nm in diameter and 1-3 mu m in length. At a small content of zinc acetate(1 mol per 100-500 mol of resorcinol), ZnO in composites is XRD amorphous and does not form individual particles. The ZnO doped chars are pure nanoporous at a minimal ZnO content and nano-mesoporousor nano-meso-macroporous at a higher ZnO content. (C) 2014 Elsevier B. V. All rights reserved.