Short composite nanofibers were fabricated by electrospinning polymer/TiO2 nanoparticle solutions of 13 wt. % cellulose acetate as a polymer under a voltage of 5.5 kV and at a flow rate of 0.1 mu L/min, and the nanoparticles could be added in concentrations as high as 50 wt. %. The length of the short composite nanofibers was significantly decreased from 112 to 70 mu m by the addition of at least a 5 wt. % concentration of nanoparticles, and it gradually continued to decrease as the nanoparticle concentration was increased. The length of the short composite nanofibers with a low concentration of nanoparticles was affected by the surface charge of the nanoparticles, and negatively charged nanoparticles readily dispersed to the negatively charged polymers in solution, which resulted in an elongation of the fabricated short composite nanofibers. (C) 2014 Elsevier B.V. All rights reserved.