Perovskite-structured oxygen carriers of the type CaxMn1-yMyO3-delta (M = Mg, Ti) have been investigated for the CLOU process. The oxygen carrier particles were produced by spray-drying and were calcined at 1300 degrees C for 4 h. A batch fluidized-bed reactor was used to investigate the chemical-looping characteristics of the materials. The effect of calcium content, dopants (Mg and Ti), and operating temperature (900, 950, 1000, and 1050 degrees C) on the oxygen uncoupling property and the reactivity with CH4 in the presence and absence of SO2 was evaluated. In addition, the attrition resistance and mechanical integrity of the oxygen carriers were examined in a jet-cup attrition rig. All of the investigated perovskite-type materials were able to release gas phase oxygen in inert atmosphere. Their reactivity with methane was high and increased with temperature and calcium content, approaching complete gas yield at 1000 degrees C. The reactivity decreased in the presence of SO2 for all of the investigated oxygen carriers. Decreasing the calcium content resulted in a less severe decrease in reactivity in the presence of SO2 with the exception of materials doped with both Mg and Ti, for which a higher resistance to sulfur deactivation could be maintained even at higher calcium contents. The drop in reactivity in the presence of SO2 also decreased At higher temperatures, and at 1050 degrees C, the decrease in the reactivity of the Mg- and Ti-doped material was minimal. Sulfur balance over the reactor system indicated that the fraction of the introduced SO2 that passed through the reactor increased with temperature. It was shown that it is possible to regenerate the oxygen carriers during reduction in the absence of SO2. Most of the materials also showed relatively low attrition rates. The results indicate that it is possible to modify the operating conditions and properties of perovskite-type oxygen carriers to decrease or avoid their deactivation by sulfur.