Here we report a water-soluble acrylamide sulfonate copolymer for inhibiting shale hydrate formation. The copolymer, denoted as PANAA, was synthesized via copolymerization of acrylamide (AM), N,N-diallylbenzylamine (NAPA), acrylic acid (AA), and 2-(acrylamide)-2-methylpropane-1-sulfonic acid (AMPS). The performance of this new water-soluble copolymer for inhibiting shale hydration was investigated for the first time. The retention ratio of apparent viscosity of 2 wt % PANAA solution can reach 61.6% at 130 degrees C and further up to 72.2% with 12 000 mg/L NaCl brine. The X-ray diffraction studies show that the addition of copolymer PANAA (5000 mg/L), in combination with a low loading of KCl (3 wt %), remarkably reduces the interlayer spacing of sodium montmorillonite (Na-MMT) in water from 19.04 to 15.65 angstrom. It has also found that these copolymer solutions, blending with KCl, can improve the retention of indentation hardness from 22% to 74% and increase the antiswelling ratio up to 84%. All results have demonstrated that the PANAA copolymer not only has excellent temperature-resistance and salt-tolerance but also exhibits a significant effect on inhibiting the hydration of clays and shale.