Single-walled carbon nanotube (SWCNT) was used as an electrode catalyst for an all vanadium redox flow battery (VRFB). The electrochemical property of SWCNT towards VO2+/VO2+ and V3+/V2+ was carefully characterized by cyclic voltammetric (CV) and electrochemical impedance spectroscopy (EIS) measurements. The peak current values for these redox pairs were significantly higher on the modified glassy carbon electrode compared with those obtained on the bare electrode, suggesting the excellent electrochemical activity of the SWCNT. Moreover, it was proved that the anodic process was more dependent on the surface oxygen of the SWCNT than the cathodic process through changing its surface oxygen content. Detailed EIS analysis of different modified electrodes revealed that the charge and mass transfer processes were accelerated at the modified electrode-electrolyte interface, which could be ascribed to the large specific surface area, the surface defects and the oxygen functional groups of the SWCNT. The enhanced battery performance effectively demonstrated that the SWCNT was suitable to serve as an electrode catalyst for the VRFB. (C) 2012 Elsevier Ltd. All rights reserved.