The activity and stability of carbon supported palladium (Pd/C) nanoparticles decorated with a submonolayer of bismuth (Bi) for formic acid (FA) electro-oxidation was investigated herein. The FA electro-oxidation activity enhancement of Bi decorated Pd/C was evaluated electrochemically using a rotating disk electrode configuration by linear sweep voltammetric and chronoamperometric measurements. Commercial Pd/C was decorated by irreversible adsorption of Bi via a simple gas controlled surface potential modulation technique, and the coverage of Bi adatoms as measured by cyclic voltammetry was controlled in the range of 30-87%. An optimal Bi coverage was observed to be 40%, resulting in a favorable decrease in the FA onset potential by greater than 0.1 V and increase in electro-oxidation current density from 0.25 mA cm(SA)(-2) to 0.55 mA cm(SA)(-2) at 0.2 V vs. RHE, compared to commercial Pd/C. The results indicate that Bi decorated Pd nanoparticles have excellent properties for the electro-oxidation of FA, i.e. high electro-catalytic activity and excellent stability, due to sustained promotion of dehydrogenation pathway attributed to the electronic effect, thereby promoting FA adsorption in the CH-down orientation. Based on no significant shifting in the CO stripping peak position, minimal impact of Bi on the Pd-CO bond strength is observed. Chronoamperometry results show much better long-term electro-catalytic activity for Bi decorated Pd nanoparticles attributed to shielding of surface Pd atoms by Bi and reducing Pd dissolution. (C) 2013 Elsevier Ltd. All rights reserved.