Aluminum bipolar plates offer good mechanical performance and availability for mass production while allow up to 65% lighter than stainless steel. To improve the corrosion resistance and surface electrical conductivity of aluminum bipolar plates, several coatings, including TiN, CrN, C, C/TiN and C/CrN, are deposited on aluminum alloy 5052 (AA-5052) by close field unbalanced magnetron sputter ion plating. Scanning electron microscope (SEM) results show that the coatings containing carbon layer are denser than TiN and CrN. Although the potentiodynamic test results show improved corrosion resistance by all the coatings, the potentiostatic test results reveal different stability of these coatings in PEMFC environments. Comparing the SEM images of these coatings after potentiostatic test, C/CrN multilayer coating exhibits the best stability. C/CrN multilayer coated AA-5052 has the lowest metal ion concentration after potentiostatic test, being 11.12 ppm and 1.29 ppm in PEMFC cathodic and anodic environments, respectively. Furthermore, the interfacial contact resistance (ICR) of the bare AA-5052 is decreased from 61.58 m Omega-cm(2) to 4.08 m Omega-cm(2) by C/CrN multilayer coating at the compaction force of 150 N-cm(-2). Therefore, C/CrN multilayer coating is a good choice for surface modification of aluminum bipolar plate. Crown Copyright (C) 2014, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.