High temperature steam electrolyzers, taking advantage of high temperature heat, can produce more hydrogen by using less electrical energy than low temperature electrolyzers. This paper presents an experimental study on hydrogen production by using a 200 W solid oxide stack working in reverse mode. A thermodynamic study of the process was performed by measuring the heat and mass balance of stack at different operating conditions. Different definitions of efficiency were used to highlight the limit and potential of the process. The I-V curve, the flow rate measurements and the GC analysis on outlet flows were used to calculate the hydrogen and oxygen productions. In addition, the influence of steam dilution, water utilization and operating temperature on conversion efficiency and stack's thermal balance was evaluated. With this aim, the tests were performed at three operating temperature (700 degrees C, 750 degrees C and 800 degrees C) over a range of steam inlet concentration from 50% to 90% and water utilization up to 70%. The hydrogen and oxygen flows produced by electrolysis, at different loads, were directly measured after water condensation: net flows up to 2.4 ml/(min cm(2)) of hydrogen and 1.2 ml/(min cm(2)) of oxygen were measured and compared to the theoretical ones, showing a good agreement. Copyright (C) 2014, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.