This pioneering study characterized the chemical, physical and mineralogical aspects of the Urucum Standard manganese ore typology, and evaluated some of its metallurgical characteristics, such as the main mineral heat decompositions, and the particle disintegration at room temperature and under continuous. heating. A one-ton sample of ore was received, homogenized and quartered. Representative samples were collected and characterized with the aid of techniques, such as ICP-AES, XRD, SEM-EDS, BET and OM. Representative samples with particle sizes between 9.5 mm and 15.9 mm were separated to perform tumbling tests at room temperature, and thermogravimetry tests for both air and nitrogen constant flow at different temperatures. After each heating cycle, the mechanical strength of the ore was evaluated by means of screening and tumbling procedures. The Urucum Standard typology was classified as an oxidized anhydrous ore, with a high manganese content (similar to 47%). This typology is mainly composed of cryptomelane and pyrolusite; however there is a significant amount of hematite. The Urucum Standard particles presented low susceptibility to disintegration at room temperature, but as temperature increased, susceptibility increased. No significant differences were observed between the tests done with the air or nitrogen injections. (C) 2013 Elsevier B.V. All rights reserved.