Here, we report the effect of temperature on the extent of hydrazine reduction of graphene oxide in N,N-dimethylformamide (DMF)/water (80/20 v/v) and the dispersibility of the resultant graphene in DMF. The highly reduced graphene oxide (HRG) had a high C/O ratio and good dispersibility in DMF. The good dispersibility of HRGs is due to the solvation effect of DMF on graphene sheets during the hydrazine reduction, which diminishes the formation of irreversible graphene sheet aggregates. The dispersibility of the HRGs was varied from 1.66 to 0.38 mg/mL when the reduction temperature increased from 25 degrees C to 80 degrees C. The dispersibility of the HRGs was inversely proportional to the electrical conductivity of the HRGs, which varied from 17,400 to 25,500 S/m. The relationships between the C/O ratio, electrical conductivity, and dispersibility of the HRGs were determined and these properties were found to be easily controlled by manipulating the reduction temperature. (C) 2012 Elsevier Inc. All rights reserved.