Thermoelectric CaMn0.98Nb0.02O3-delta single crystals were grown from sintered polycrystalline material using the traveling-solvent floating zone (TSFZ) method. The floating-zone furnace was operated at over-pressure using an Ar/O-2 mixture to prevent evaporation during the growth process. Six twin-domain variants were detected with single-crystal X-ray diffraction (XRD) and confirmed by electron diffraction (ED) and high-resolution transmission electron microscopy (HRTEM). The Seebeck coefficient (S) of the single-crystalline material indicates n-type semiconducting behavior. Within 10 K < T < 125 K a negative peak in S is observed, known to be characteristic of antiferromagnetic ordering. The ferromagnetic long-range ordering, expected on the basis of double exchange between Mn4+ and doped Mn3+ species, thus appears to remain suppressed in the single-crystalline material. (c) 2013 Elsevier B.V. All rights reserved.