An interesting new material based on a Nafion (R) membrane doped with a sulfated-zirconia filler is presented. This filler is unique in that the filler itself can contribute to the proton conductivity due to the presence of acidic functionalities on the surface of the filler. The presence of the filler in the membrane results in the deprotonation of Nafion (R)'s acid moieties as indicated by the absence of the acid mode at 1475 cm(-1) in the FTIR spectrum. Spectra from DSC, DMA and broadband electric spectroscopy (BES) show the presence of several molecular transitions, two of which are detected in the BES permittivity profiles. The membrane exhibits a reasonably high conductivity (3 x 10(-3) S cm(-1) at 120 degrees C) even in completely dry conditions, which makes it a promising material for an anhydrous fuel cell. The conductivity behaviour exhibits a mix of Arrhenius and VTF behaviours and is closely tied to the dielectric relaxations. (C) 2011 Elsevier B.V. All rights reserved.