Carbon-coated clustered LiMn0.71Fe0.29PO4 (c-LMFP) nanoparticles are prepared from ball-milling with a mixture of similar to 40 nm thick LMFP nanoplates obtained by polyol method and carbon black. The clustered nanocomposite structure of c-LMFP turns out to have advantages of improved volumetric energy density and electrochemical performance. The c-LMFP exhibits increased tap density of 0.9 g cm(-3), compared with the as-prepared LMFP nanoplates (0.6 g cm(-3)), providing with high volumetric discharge capacity of 243 mA h cm(-3) at 0.1C and 128 mA h cm(-3) even at 7C at 21 degrees C. At elevated temperature (60 degrees C), the capacity retention of c-LMFP remains excellent (100% of its initial capacity (165 mA h g(-1)) at the same cycling condition as 21 degrees C). In sharp contrast, capacity of carbon-coated LiMnPO4 (c-LMP) exhibits volumetric discharge capacity of 72 mA h cm(-3) at 5C and decays rapidly at 60 degrees C after 40 cycles (capacity retention of 58%). The better cycling stability of c-LMFP than that of c-LMP is believed to be associated with mitigated Mn2+ dissolution by Fe2+ substitution. (C) 2012 Elsevier B.V. All rights reserved.