A critical analysis was carried out for the purpose of understanding the role of subcolloidal (nanosized) (alumino)silicate precursor species in the early stage of crystallization of zeolites in heterogeneous systems (hydrogels). The formation and evolution of these subcolloidal species in both the solid and the liquid phases were investigated by various experimental methods such a scanning electron microscopy (SEM, FE-SEM), transmission electron microscopy, atomic force microscopy, particle size analysis, pH measurement, atomic absorption spectroscopy, and dynamic light scattering, after careful separation of intermediates from reaction mixture by two-step centrifugation treatment. The results revealed that a chain of processes (i) the formation of low-molecular-weight (LMW) silicate species, by dissolution of Al-enriched amorphous silica, and their aggregation into about 3 nm sized primary precursor species (PPSs), (ii) the formation of larger (similar to 3 to similar to 5 nm sized) silicate precursor species (LSPSs) by a rapid aggregation/coalescence of PPSs, (iii) the formation of "gel" (primary amorphous precursor) by a random aggregation of LSPSs at room temperature, and (iv) the formation of the worm-like particles (secondary amorphous precursor) occurred in the solid phase during heating of the reaction mixture (hydrogel) from room temperature to 170 degrees C. It is interesting that almost the same processes occur in the liquid phase but with decreased rate according to the relative low concentration of LMW silicate species. With the above described findings, it is highly expected that the manipulation of crystallization pathway through controlling the formation/evolution of precursor species in the initial stage of the process can be achieved.