Single crystals of pure and L-tartaric acid (LTA) C4H6O6 doped ammonium dihydrogen phosphate (ADP) (NH4) H2PO4 were grown by slow evaporation solution technique (SEST) at ambient conditions. Powder X-ray diffraction (PXRD) analysis was carried out to confirm the crystal structure and no additional phase was observed due to doping except a systematic variation in peak intensities. Fourier transform infrared spectral analysis was done to examine the presence of various functional groups in the grown crystals. UV-VIS-NIR spectroscopic analysis was carried out to see the change in optical transparency of pure ADP and crystals due to LTA with different doping concentrations. Second harmonic generation (SHG) efficiency measurement was done to examine the enhancement in the nonlinear optical characteristics of the grown crystals. The effect of LTA dopant on crystal morphology, thermal and mechanical properties of ADP have also been presented in this paper. The above studies reveal the effect of incorporation of LTA into the lattice of ADP crystals. (C) 2014 Elsevier B.V. All rights reserved.