Thermomechanical cycling under constant stress on transformation behavior, fatigue life and deformation behavior of a Ti50Ni40Cu10 (at%) alloy annealed at different temperatures were investigated. It was found that annealing temperature has obvious effect on transformation temperatures, fatigue life and deformation behavior of the alloy cycled to failure.