The micro-mechanisms involved in the gamma/gamma' rafted microstructure built up at 1050degreesC in <001> oriented MC2 superalloy single crystals are analysed by means of SEM, post mortem and in situ TEM observations. The creation and propagation modes of moving dislocations evidence the important role of the misfit dislocation network as well as the strength of the gamma/gamma' interfaces.