The superplastic characteristics and diffusion bonding behaviors were investigated in commercial 7475 aluminum alloy and AZ31 magnesium alloy sheets. In this study, the presently used materials behaved in a superplastic manner at similar to773 K (7475Al) and similar to523 K (AZ31). Then, by the theoretical relationship between pressure and time, these materials were successfully diffusion bonded at the superplastic temperatures. The bonding strength was more than 65 MPa. The experimental bonding conditions in high quality joining, times and pressures, were good agreed with prediction analysis.