This work was devoted to characterize the transformations in a Cu-9Ni-6Sn alloy (weight percent) using the differential scanning calorimetry (DSC) technique. Both solution treatment and precipitation hardening transformations were studied. Different previous conditions were imposed to the samples tested in DSC, in order to allow a more clear understanding of the outputs.