Polycrystalline samples of NiAl have been deformed in torsion in the temperature range 800K - 1300K. Deformation is accompanied by dynamic recrystallization, which with increasing temperature changes from continuous to discontinuous mode. Emphasis was put on the occurrence of continuous dynamic recrystallization, which will be discussed with respect to texture and microstructure.