Large scale computer simulations suggest that in nanocrystalline metals grain boundaries act as source and sink for dislocations. This suggestion has been the motivation for developing a new in-situ X-ray diffraction technique that allow peak profile analysis of several Bragg diffraction peaks during tensile deformation. Synergies between simulations and experiments are discussed including new applications of the in-situ technique.