In this work fluorinated Diamond Like Carbon (DLC) films have been grown with different CF4 concentrations and have been studied by electrical DC measurements in a temperature range from 30 to 300 K. It was found that the samples grown with lower CF4 concentration show a small rectification, with a potential barrier lower than 0.3 V. The bulk conduction shows a trap-controlled Space Charge Limited Current (SCLC), with characteristic trap energy between 0.08 and 0.13 eV, confirmed by the differential conductivity analysis. The activation energy (ranging from 50 to 140 meV) is also dependent on the sample fluorine concentration, decreasing with the fluorine concentration increase.