The effect of cold wire drawing on texture of industrial low carbon steel wire was investigated. On the other hand, the mechanism of recrystallization of drawn-wire was studied during different isothermal annealing below 723 degrees C. The structural evolution of wire was studied by optical microscopy, SEM, EBSD and X-Ray diffraction. From this study, a fiber texture was observed in deformed wire. However, a recrystallization reaction occurs after critical temperature during annealing.