We demonstrate a facile route to decorate the surface of networked single walled carbon nanotubes (SWNTs) with silver nanoparticles (Ag NPs). The method is based on utilization of either spherical poly(styrene-b-4vinylpyridine) (PS-b-P4VP) or cylindrical poly(styrene-b-acrylic acid) (PS-b-PAA) copolymer micelles capable of stabilizing nanotubes in solution and subsequently forming a thin and uniform block copolymer/SWNTs composite film upon spin coating. The selective doping of silver acetate into either P4VP or PAA domains in a thin composite film, followed by thermal treatment, results in the formation of Ag NPs in the cores of micelles. Further heat treatment at 500 degrees C sufficiently high for degrading both block copolymers allows us to fabricate a thin SWNTs network in which Ag NPs are efficiently deposited on the surface of nanotubes. A sharp surface plasmon absorption band around 400 nm of the networked SWNTs with Ag NPs confirms the presence of Ag NPs with narrow distribution in their size. (C) 2009 Elsevier Ltd. All rights reserved.